Beating the heat: Oxidation in novel coating material for aircraft gas turbine engines

Unfortunately, existing coating layers cannot fully prevent this oxidization to SiO₂ because oxygen can permeate through microscopic cracks in these layers or by simple diffusion.

To address this issue, some scientists have focused on using ytterbium silicide (Yb-Si) as a coating material because Yb-Si can reach high melting points and their oxides are mainly Yb-silicates, which remain attached as an oxide layer and do not evaporate easily. However, not much is known about the fundamental phenomena that take place in these materials at high temperatures in either air or water vapor environments.

In a recent study published in Intermetallics, a team of scientists-including Junior Associate Professor Ryo Inoue, Assistant Professor Yutaro Arai and Professor Yasuo Kogo from Tokyo University of Science, and Senior Researcher Takuya Aoki from the Japan Aerospace Exploration Agency (JAXA)-set out to understand the oxidation mechanisms in Yb-Si. They conducted a variety of experiments to gain insight into the oxidation behavior (and degradation) of different Yb-Si coatings at high temperatures under three types of atmospheres: air, water vapor, and a mixture of both.

Through X-ray diffraction analysis, energy dispersive spectroscopy, and scanning electron microscopy, the scientists were able to accurately visualize and quantify the morphology and composition of the Yb-Si samples before and after the heat exposure tests. One of the main findings was that the Yb to Si ratio was a major player in defining the oxidation behavior of the material; Yb₅Si3 oxidized more than Yb₃Si₅ because of the preferential oxidation of Yb in silicide. Moreover, the amount of oxide decreased considerably in more water vapor-rich atmospheres.

Most importantly, the researchers explored the mechanisms by which ytterbium content can affect the formation of SiO₂. "After heat exposure of both silicides in steam, we found SiO₂ in Yb₅Si₃, whereas Si was actually still present in Yb₃Si₅," remarks Dr Inoue, who led the study. "Our analyses indicate that SiO₂ growth is suppressed in Yb₃Si₅ because SiO₂ partakes in, and is the limiting factor of, reactions that form Yb-silicates," he adds. Though the exact intermediate reactions that lead to the formation of the various Yb-silicates are not completely understood yet, the team presented two highly possible reaction pathways. This will likely be clarified through future studies with even more detailed characterization techniques.

Overall, this study provides meaningful insight into what happens during the oxidation of Yb-Si, which will help in the development of protective coatings for aero gas-turbine engines. "If a coating that can withstand harsher environments can be realized, engine parts will become more heat resistant, which naturally leads to higher engine efficiency," remarks Dr Inoue.

Hopefully, further advances in coating technology will reduce aerial transportation costs and fuel consumption, making flying cheaper and less harmful to the environment.